Stabilized composition comprising{60 -olefin polymers and melamine

ABSTRACT

The resistance of Alpha -olefin polymers to copper induced oxidation is improved by adding thereto 0.01 to 2 percent melamine along with conventional antioxidants and light stabilizers. The efficiency of the melamine as a stabilizer is improved if the particle size is below about 55 Mu .

United States Patent Kutner 1 May 30, 1972 [54] STABILIZED COMPOSITION [56] References Cited COMPRISINGa-OLEFIN POLYMERS UNI D STAT PATE S AND MELAMINE TE ES NT 3,l8l,971 5 1965 R ..260 45.8 [72] Inventor: Abraham Kutner, Wilmington, Del. I ayner 5 [73] Assignee: Hercules Incorporated, Wilmington, Del. FOREIGN PATENTS OR APPLICATIONS [22] Filed: July 8 1970 43/29,756 3/1968 Japan [21] Appl. No.: 53,275 Primary Examiner-Donald E. Czaja Assistant Examiner-V. P. Hoke Related Animation Data Attorney-Edwin H. Dafter, Jr. [63] Continuation-impart of Ser. No. 625,308, Mar. 23,

1967, abandoned. [571 ABSTRACT The resistance of a-olefin polymers to copper induced oxida- [52] U.S. Cl ..260/45.8 N, 1 17/232, 260/45.7 S, ion is improved by adding thereto 01 to 2 percent melamine 260/45-85 260/4595 along with conventional antioxidants and light stabilizers. The [51] Int. Cl. ..C08f45/60 ffi i f the mdamine a Stabilizer is improved if the [58] Field of Search ..260/45.8 N, 41 C, 45.85, 45.78, particle Size is below about 55,, 260/4595 6 Claims, No Drawings This application is a continuation-in-part of my copending US. application Ser. No. 625,308, filed Mar. 23, 1967 and now abandoned.

This invention relates to propylene polymer compositions suitable for use as coating materials for copper articles.

It is known that olefin polymers such as stereoregular polypropylene undergo rapid oxidative degradation and become brittle and useless when in the presence of copper, particularly at elevated temperatures. This degradation does not appear to be prevented by even the best stabilizer-antioxidant systems known in the art. Since these polymers otherwise have excellent mechanical and electrical properties which make them excellent candidates for such uses as electrical wire insulation, electrical condensers, and moldings with copper inserts, the art has found it necessary to seek out ways to prevent this degradation.

The most likely method for preventing copper-induced degradation is by the addition of a copper antagonist thereto and several such additives have been disclosed by the prior art. For example, US. Pat. No. 3,239,484 teaches the use of oxanilide in conjunction with a crotonaldehyde-phenol condensation product to retard metal induced degradation. US. Pat. No. 3,181,971 teaches use of certain aliphatic and aromatic amines having boiling points greater than about 200 C. in combination with phenolic antioxidants and an organic compound containing divalent sulfur. U.S. Pat. No. 3,296,188 teaches the use of hydrazone compounds containing as a substituent a six membered heterocyclic nitrogen radical, a phenol and, optionally, an organic sulfur compound.

The additives disclosed by the prior art for improving resistance to copper induced degradation perform effectively but are subject to other objections. For example, oxanilide and oxamide are difficult to disperse uniformly in the polymer and affect electrical properties adversely. The hydrazones are not usually available commercially in quantity and are thus quite expensive.

Now in accordance with this invention it has been found that the oxidation stability of stereoregular polyolefins in the presence of copper can be substantially increased by the addition thereto of a specified amount of melamine (2,4,6 striazine) in addition to conventional heat stabilizers. More specifically, the invention is a composition which exhibits good resistance to oxidative degradation in the presence of copper which comprises a heat stabilized polymer of an olefin containing as a copper antagonist, about 0.01 to 2 percent melamine, preferably 0.03 to 0.5 percent based on the weight of the olefin polymer.

Melamine shows a number of advantages over copper inhibitors disclosed in the art. It is not volatile under the conditions of use, shows little tendency to exude from the polymer, and its presence in the polymer does not adversely afiect electrical properties. Additionally, it is readily available in carload lots at a low price. It has been found to disperse well in the polymer even though it is not soluble therein.

The polymers to which the instant invention is applicable include the crystalline homopolymers of ethylene and a-olefins having three to six carbon atoms as well as copolymers of any one of these olefins containing a minor proportion of at least one other of the group. Thus, they include, e.g., polyethylene, polypropylene, poly(butene-l poly( 3-methyl butene-l and crystalline copolymers thereof. In particular, the invention is applicable to homopolymers of propylene and those copolymers containing up to about 25 percent ethylene which are still predominantly crystalline. These can be either of the random (statistical) type or the so-called block copolymers.

The a-olefin polymers with which the present invention is concerned are stabilized against the degradative efiects of heat by known antioxidant or heat stabilizer systems. Exemplary of such systems are the synergistic combinations of hindered phenols and organic compounds containing divalent sulfur. These materials are normally employed in concentra- I mula:

tions of about 0.01 to 2 percent, preferably 0.05 to 0.5 percent.

Exemplary phenolic antioxidants are those containing more than one phenolic residue and having a sterically blocking group on at least one carbon atom adjacent to each phenolic hydroxyl group as represented by the following structural forwhere X is n 1110110- or disulfide group or is and the R substituents on the phenolic nuclei are aliphatic or cycloaliphatic hydrocarbon radicals, alkoxy groups or hydrogen, with at least one branched or blocking hydrocarbon group 011110 to each hydroxyl group on a phenolic nucleus, and R and R are alkyl radicals, hydroxyaryl radicals, hydroxyaryl substituted hydrocarbon radicals, cycloalkyl radicals or hydrogen atoms. Examples of suitable phenolic antioxidants in the above class are those formed by condensing a phenol with an aldehyde or ketone or with a sulpher monoor dichloride. For an exhaustive listing of useful phenolic antioxidants in this class and discussion of their preparation, reference can be had to Rayner, U.S. Pat. No. 3,181,971.

Another type of polyphenolic compound which has been found useful is the pentaerythritol ester of B-phenylpropionic aciclhaving the structural formula 7 where R is a branched, blocking hydrocarbon radical and R is a hydrocarbon radical or hydrogen.

Other useful phenolic compounds are the mesitylene trisphenols of thefonnula;

CHsa CH -CH2 R" I CH3 OH OH where R and R are as described for the pentaerythritol esters.

Among all of the phenolic compounds embraced in the above classes, the following have been found to be particularly effective in combination with melamine according to this invention: pentaerythritol tetra-3(4-hydroxy-3,S-di-t-butylphenyl propionate), crotonaldehyde--3-methyl -6-t-butylphenol condensation product, butyraldehyde--3-methyl-6- t-butylphenol condensation product, 3-methyl-6-t-butylphenol--sulfur dichloride condensation product, and 2,4,6- tris( 4-hydroxy-3,S-di-t-butylbenzyl) mesitylene.

The main classes of organic sulfur compounds which are used are (l) mercaptans, thioethers and disulfides and (2) diwhere R is an alkyl radical having about two to five carbon atoms and R is an alkyl radical having about 10 to 20 carbon atoms. Preferred examples of this class are the thiodipropionic and thiodibutyric acid diesters such as dilauryl thiodipropionate, distearyl thiodipropionate, dilauryl thiodibutyrate, and distearyl thiodibutyrate.

A complete discussion of useful sulfur-containing compounds, all of which are useful herein, can be found in the Rayner patent cited above.

For best results, the melamine should be reduced to a small particle size. The useful size range is from about 1 to 40011., preferably 1 to 5511., or even more preferably 1 to 1011.. This material, as supplied is frequently in larger particles than the above specified ranges. it can readily be reduced to the desired size by any known method such as by ball milling, roll milling. disc milling orjet milling. Ultrasonic methods can also he used.

The melamine can be added to the polymer by known means. A preferred method is by adding fine particles thereof to the polymer and mixing in the molten state on a Banbury mixer or the like. In some cases the incorporation can be carried out in the extruder. Deposition of the additive from a solution or dispersion in a volatile solvent is another useful alternative, but in this case, relatively vigorous agitation is necessary during solvent removal to prevent large crystal deposition.

1t will usually happen that the polymer will already be compounded with the antioxidant and stabilizer additives as it is supplied by the manufacturer since it is usually desirable to have the same present during preparation of commercial forms of polymer. If not, these can be added simultaneously with the melamine, employing the same methods.

In the following examples, which illustrate the invention, parts and percentages are by weight unless otherwise specified. Samples were prepared for testing by incorporating 1.4 percent of electrolytic grade copper powder in the polymer in a Brabender Plastograph at 190 C. under a nitrogen atmosphere, and fluxing the mixture for 3 minutes. After removing the polymeric composition from the plastograph, it was pressed flat between aluminum plates and cooled rapidly. A portion of this material was then pressed into a 10- mil sheet for 1.5 minutes at 180 C. in an electrically heated press. Samples of this sheet (0.100 t 0.002 g.) were then tested in an oxygen absorption tube immersed in a constant temperature bath at 140 C., using a mercury leveling device to follow absorption of oxygen. The method is described in detail by R.H.Hansen, et al., in the Journal of Polymer Science, Part A, 2, 587 (1964). The end of the induction period is marked by the absorption of 1.0 ml. of oxygen, at which time the mechanical and electrical properties have failed.

EXAMPLES l- Samples were homopolypropylene prepared and containing 0.25

thiodipropionate (DSTDP), 0.25 percent of the condensation product of 1 mole crotonaldehyde and 3 moles of 3-methyl-6- t-butylphenol and melamine at the level indicated in the table. Test results clearly show the improved copper resistance im- 5 parted by the melamine as well as the beneficial effect ofsmall particle size. Test results (average of duplicate determinations) are as follows:

Melamine particle size Melamine Induction content, time, Example No. Max. Min. Average percent hours Control O 425 1 100 0. 125 JO 1 25 0. 25 285 55 1 12 0. 25 395 1 3. 5 0. 25 390 55 1 12 0.05 265 EXAMPLES 6-16 Anti- Sulfur lCxnnIpln nxl lvfemnl'urlercnnl. induction Nu. dnnl. wnl. pound cunt nmlumlnn time, hrs.

(H)lll,rnl A 0.25 HHIIH 0 25 21) l A ll. 25 DH'IIH ll. 25 0. 5 330 l! ll. 5 DS'IDI 0. 25 0. .25 130 (1 (1.5 DS'll)! 0.25 0. 25 520 D 0. 25 l)LT])l 0. 5 0. 25 340 1) 0. 25 DLIDP 0. 5 0. 25 375 C 0. 25 DLIDB 0. 25 0. 25 400 C 0. 25 DSS 0. 25 0. 25 275 A 0.5 SM 0.5 0.25 225 A 0.5 DSDS 0.5 0.25 200 D 0. 25 DLIDB 0. 25 0. 25 375 D 0. 25 DHS 0. 25 0. 25 200 Control. C 0.25 DSTDP 0. 25 20 EXAMPLES 17-22 Anti- Average oxi- Pct-cent particle Induction Example N o. dant Percent melamine size time (his) D 0. 25 0.1 12;; 390 D 0. 25 0. 25 12;; 390 D 0. 25 0. 5 12 1 390 E 0. 25 0.1 1211 154 E 0. 25 0. 25 12;: 184 E 0. 5 0. 25 12 205 Control E 0. 5 26 EXAMPLES 23-24 A copolymer of ethylene and about 1.4 percent butene-l containing about 1.4 percent copper dust therein was formulated with about 0.25 percent DSTDP, about 0.25 percent of the condensation product of 1 mole crotonaldehyde and 3 moles of 3-methyl-6-t-butylphen0l and either 0.25 or 0.5 percent melamine of 12 1. average particle size. These specimens were subjected to the 0 absorption test as described above except that the test was conducted at 130 C. Both specimens 75 (0.25 and 0.5 percent melamine) failed after about 260 hours.

A control sample of the same polymer, containing no melamine, failed after about 60 hours.

An interesting ancillary benefit of this invention is that it increases the heat stability of the olefin polymers in contact with inorganic reinforcing fillers such as asbestos and talc. These materials have been found to contribute to relatively rapid degradation of the polymer apparently due to the presence of trace amounts of copper salts. The degradative effect of these salts is also overcome by the melamine.

In addition to basic melamine, it has been found that certain salts of melamine also contribute to increased copper stability.

. Exemplary, though not all inclusive of such salts, are the lzl salt of melamine with thiodipropionic acid, the 1:1 salt of melamine with salicylic acid, and the 2:1 salt of melamine with sulfuric acid.

What i claim and desire to protect by Letters Patent is:

l. A composition comprising a heat-stabilized polymer of an a-olefin having two to six carbon atoms containing, as a copper antagonist, about 0.0] to 2 percent melamine, based on the weight of said a-olefin polymer.

2. A composition which exhibits good resistance to oxidative degradation in the presence of copper which comprises a polymer of an olefin having two to six carbon atoms containing, based on the weight of said polymer, about 0.01 to 2 percent of melamine, about 0.01 to 2 percent of phenolic antioxidant having more than one phenolic residue and having sterically blocking group on at least one carbon atom adjacent to each phenolic hydroxyl group, and about 0 to 2 percent of an organic sulfur compound having a molecular weight of at least about 250 selected from the class consisting of (l) mercaptans, and disulfides, and 2) diesters ofthiodialkanoic acids.

3. A composition which exhibits good resistance to oxidative degradation in the presence of copper which comprises a polymer of an olefin having two to six carbon atoms containing, based on the weight of said polymer, about 0.01 to 2 percent of melamine, about 0.01 to 2 percent of a phenolic antioxidant having more than one phenolic residue and having a sterically blocking group on at least one carbon atom adjacent to each phenolic hydroxyl group, and about 0 to 2 percent of an organic sulfur compound selected from the class consisting of (l) distearyl thiodipropionate, (2) dilauryl thiodipropionate, (3) dilauryl thiodibutyrate (4) distearyl sulfide, (5) stearyl mercaptan, (6) distearyl disulfide, and (7) dihexadecyl sulfide.

4. The composition of claim 3 wherein the phenolic antioxidant is selected from the class consisting of l) the condensation product of about 1 mole of crotonaldehyde and about 3 moles of 3-methyl-6-t-butyl phenol, (2) the condensation product of about 1 mole of butyraldehyde and 2 moles of 3- methyl-G-t-butylphenol, 3) pentaerythritol tetra-B( 4-hydroxy-3,5-di-t-butylphenyl)propionate, (4) the condensation product of about 1 mole of SCl with about 2 moles of 3- methyl-6-t-butylphenol, and (5) 2,4,6-tris(4-hydroxy-3,5-di-tbutylbenzyl)mesitylene.

5. The composition of claim 3 where the olefin polymer is selected from the class consisting of polypropylene and crystalline copolymers of propylene with up to about 25 percent ethylene.

6. The composition of claim 3 where the olefin polymer is selected from the class consisting of polyethylene and copolymers of ethylene with minor portions of a second aolefin. 

2. A composition which exhibits good resistance to oxidative degradation in the presence of copper which comprises a polymer of an olefin having two to six carbon atoms containing, based on the weight of said polymer, about 0.01 to 2 percent of melamine, about 0.01 to 2 percent of phenolic antioxidant having more than one phenolic residue and having sterically blocking group on at least one carbon atom adjacent to each phenolic hydroxyl group, and about 0 to 2 percent of an organic sulfur compound having a molecular weight of at least about 250 selected from the class consisting of (1) mercaptans, and disulfides, and (2) diesters of thiodialkanoic acids.
 3. A composition which exhibits good resistance to oxidative degradation in the presence of copper which comprises a polymer of an olefin having two to six carbon atoms containing, based on the weight of said polymer, about 0.01 to 2 percent of melamine, about 0.01 to 2 percent of a phenolic antioxidant having more than one phenolic residue and having a sterically blocking group on at least one carbon atom adjacent to each phenolic hydroxyl group, and about 0 to 2 percent of an organic sulfur compound selected from the class consisting of (1) distearyl thiodipropionate, (2) dilauryl thiodipropionate, (3) dilauryl thiodibutyrate, (4) distearyl sulfide, (5) stearyl mercaptan, (6) distearyl disulfide, and (7) dihexadecyl sulfide.
 4. The composition of claim 3 wherein the phenolic antioxidant is selected from the class consisting of (1) the condensation product of about 1 mole of crotonaldehyde and about 3 moles of 3-methyl-6-t-butyl phenol, (2) the condensation product of about 1 mole of butyraldehyde and 2 moles of 3-methyl-6-t-butylphenol, (3) pentaerythritol tetra- Beta (4-hydroxy-3,5-di-t-butylphenyl)propionate, (4) the condensation product of about 1 mole of SC12 with about 2 moles of 3-methyl-6-t-butylphenol, and (5) 2,4,6-tris(4-hydroxy-3,5-di-t-butylbenzyl)mesitylene.
 5. The composition of claim 3 where the olefin polymer is selected from the class consisting of polypropylene and crystalline copolymers of propylene with up to about 25 percent ethylene.
 6. The composition of claim 3 where the olefin polymer is selected from the class consisting of polyethylene and copolymers of ethylene with minor portions of a second Alpha -olefin. 